92-silver 8-tin-oxide vs. C14700 Copper
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while C14700 copper belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is C14700 copper.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 95 |
| Elongation at Break, % | 32 to 34 | |
| 9.1 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 25 to 65 |
| Shear Strength, MPa | 150 to 210 | |
| 160 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 240 to 320 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 85 to 250 |