92-silver 8-tin-oxide vs. C36200 Brass
92-silver 8-tin-oxide belongs to the otherwise unclassified metals classification, while C36200 brass belongs to the copper alloys. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is 92-silver 8-tin-oxide and the bottom bar is C36200 brass.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 76 to 80 | |
| 26 |
| Elongation at Break, % | 32 to 34 | |
| 20 to 53 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 62 to 110 | |
| 74 to 140 |
| Shear Strength, MPa | 150 to 210 | |
| 210 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 320 | |
| 340 to 420 |
| Tensile Strength: Yield (Proof), MPa | 120 to 300 | |
| 130 to 360 |