ACI-ASTM CA15M Steel vs. 6025 Aluminum

ACI-ASTM CA15M steel belongs to the iron alloys classification, while 6025 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is ACI-ASTM CA15M steel and the bottom bar is 6025 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
70
Elongation at Break, % 20
2.8 to 10
Fatigue Strength, MPa 330
67 to 110
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 76
26
Tensile Strength: Ultimate (UTS), MPa 690
190 to 240
Tensile Strength: Yield (Proof), MPa 510
68 to 210

Thermal Properties

Latent Heat of Fusion, J/g 270
410
Maximum Temperature: Mechanical, °C 760
160
Melting Completion (Liquidus), °C 1450
650
Melting Onset (Solidus), °C 1410
550
Specific Heat Capacity, J/kg-K 480
900
Thermal Conductivity, W/m-K 27
130
Thermal Expansion, µm/m-K 10
23

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
33
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
110

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
9.5
Density, g/cm3 7.8
2.8
Embodied Carbon, kg CO2/kg material 2.1
8.5
Embodied Energy, MJ/kg 29
150
Embodied Water, L/kg 100
1160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
6.0 to 15
Resilience: Unit (Modulus of Resilience), kJ/m3 670
33 to 310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
50
Strength to Weight: Axial, points 25
19 to 24
Strength to Weight: Bending, points 22
26 to 31
Thermal Diffusivity, mm2/s 7.2
54
Thermal Shock Resistance, points 25
8.2 to 10

Alloy Composition

Aluminum (Al), % 0
91.7 to 96.3
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 11.5 to 14
0 to 0.2
Copper (Cu), % 0
0.2 to 0.7
Iron (Fe), % 82.1 to 88.4
0 to 0.7
Magnesium (Mg), % 0
2.1 to 3.0
Manganese (Mn), % 0 to 1.0
0.6 to 1.4
Molybdenum (Mo), % 0.15 to 1.0
0
Nickel (Ni), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.65
0.8 to 1.5
Sulfur (S), % 0 to 0.040
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.15