ACI-ASTM CA15M Steel vs. AWS E320LR

Both ACI-ASTM CA15M steel and AWS E320LR are iron alloys. They have 52% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA15M steel and the bottom bar is AWS E320LR.

ACI-ASTM CA15M (J91151) Cast Stainless Steel AWS E320LR (W88022) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		20
Elongation at Break, %		34

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		76
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		690
Tensile Strength: Ultimate (UTS), MPa		580

Thermal Properties

Latent Heat of Fusion, J/g		270
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1450
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		1410
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		10
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		7.5
Base Metal Price, % relative		36

Density, g/cm³		7.8
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		2.1
Embodied Carbon, kg CO₂/kg material		6.2

Embodied Energy, MJ/kg		29
Embodied Energy, MJ/kg		87

Embodied Water, L/kg		100
Embodied Water, L/kg		220

Common Calculations

PREN (Pitting Resistance)		15
PREN (Pitting Resistance)		28

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		25
Strength to Weight: Axial, points		20

Strength to Weight: Bending, points		22
Strength to Weight: Bending, points		19

Thermal Shock Resistance, points		25
Thermal Shock Resistance, points		15

Alloy Composition

Carbon (C), %		0 to 0.15
Carbon (C), %		0 to 0.030

Chromium (Cr), %		11.5 to 14
Chromium (Cr), %		19 to 21

Copper (Cu), %		0
Copper (Cu), %		3.0 to 4.0

Iron (Fe), %		82.1 to 88.4
Iron (Fe), %		32.7 to 42.5

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		1.5 to 2.5

Molybdenum (Mo), %		0.15 to 1.0
Molybdenum (Mo), %		2.0 to 3.0

Nickel (Ni), %		0 to 1.0
Nickel (Ni), %		32 to 36

Niobium (Nb), %		0
Niobium (Nb), %		0 to 0.4

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.020

Silicon (Si), %		0 to 0.65
Silicon (Si), %		0 to 0.3

Sulfur (S), %		0 to 0.040
Sulfur (S), %		0 to 0.015