ACI-ASTM CA15M Steel vs. EN 1.3542 Stainless Steel
Both ACI-ASTM CA15M steel and EN 1.3542 stainless steel are iron alloys. Their average alloy composition is basically identical. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CA15M steel and the bottom bar is EN 1.3542 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 770 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 27 | |
| 29 |
| Thermal Expansion, µm/m-K | 10 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 | |
| 3.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 7.5 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.1 | |
| 2.0 |
| Embodied Energy, MJ/kg | 29 | |
| 29 |
| Embodied Water, L/kg | 100 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 15 | |
| 15 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 25 | |
| 26 |
| Strength to Weight: Bending, points | 22 | |
| 23 |
| Thermal Diffusivity, mm2/s | 7.2 | |
| 7.9 |
| Thermal Shock Resistance, points | 25 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.6 to 0.7 |
| Chromium (Cr), % | 11.5 to 14 | |
| 12.5 to 14.5 |
| Iron (Fe), % | 82.1 to 88.4 | |
| 82.7 to 87.5 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 1.0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.65 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.030 |