ACI-ASTM CA40F Steel vs. AISI 304N Stainless Steel

Both ACI-ASTM CA40F steel and AISI 304N stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA40F steel and the bottom bar is AISI 304N stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
190 to 360
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 13
9.1 to 45
Fatigue Strength, MPa 320
220 to 440
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 770
620 to 1180
Tensile Strength: Yield (Proof), MPa 550
270 to 850

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 750
960
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 27
16
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 7.5
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.0
3.0
Embodied Energy, MJ/kg 28
43
Embodied Water, L/kg 100
150

Common Calculations

PREN (Pitting Resistance) 14
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 94
98 to 280
Resilience: Unit (Modulus of Resilience), kJ/m3 790
180 to 1830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
22 to 42
Strength to Weight: Bending, points 24
21 to 32
Thermal Diffusivity, mm2/s 7.2
4.2
Thermal Shock Resistance, points 28
14 to 26

Alloy Composition

Carbon (C), % 0.2 to 0.4
0 to 0.080
Chromium (Cr), % 11.5 to 14
18 to 20
Iron (Fe), % 81.6 to 88.3
66.4 to 73.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 0 to 1.0
8.0 to 10.5
Nitrogen (N), % 0
0.1 to 0.16
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0.2 to 0.4
0 to 0.030