ACI-ASTM CA40F Steel vs. ASTM A228 Music Wire
Both ACI-ASTM CA40F steel and ASTM A228 music wire are iron alloys. They have 86% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CA40F steel and the bottom bar is ASTM A228 music wire.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 | |
| 710 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 | |
| 12 |
| Fatigue Strength, MPa | 320 | |
| 1280 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 2450 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 2050 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 400 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1450 |
| Melting Onset (Solidus), °C | 1390 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 27 | |
| 49 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 1.8 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 1.4 |
| Embodied Energy, MJ/kg | 28 | |
| 19 |
| Embodied Water, L/kg | 100 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 | |
| 280 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 87 |
| Strength to Weight: Bending, points | 24 | |
| 52 |
| Thermal Diffusivity, mm2/s | 7.2 | |
| 13 |
| Thermal Shock Resistance, points | 28 | |
| 79 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.4 | |
| 0.7 to 1.0 |
| Chromium (Cr), % | 11.5 to 14 | |
| 0 |
| Iron (Fe), % | 81.6 to 88.3 | |
| 98 to 99 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.2 to 0.6 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.5 | |
| 0.1 to 0.3 |
| Sulfur (S), % | 0.2 to 0.4 | |
| 0 to 0.030 |