ACI-ASTM CA40F Steel vs. AWS E240
Both ACI-ASTM CA40F steel and AWS E240 are iron alloys. They have 78% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CA40F steel and the bottom bar is AWS E240.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 13 | |
| 17 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1390 |
| Melting Onset (Solidus), °C | 1390 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 27 | |
| 15 |
| Thermal Expansion, µm/m-K | 10 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 14 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 3.0 |
| Embodied Energy, MJ/kg | 28 | |
| 42 |
| Embodied Water, L/kg | 100 | |
| 160 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 22 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 28 | |
| 28 |
| Strength to Weight: Bending, points | 24 | |
| 24 |
| Thermal Diffusivity, mm2/s | 7.2 | |
| 3.9 |
| Thermal Shock Resistance, points | 28 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.4 | |
| 0 to 0.060 |
| Chromium (Cr), % | 11.5 to 14 | |
| 17 to 19 |
| Copper (Cu), % | 0 | |
| 0 to 0.75 |
| Iron (Fe), % | 81.6 to 88.3 | |
| 58.6 to 68.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 10.5 to 13.5 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 to 0.75 |
| Nickel (Ni), % | 0 to 1.0 | |
| 4.0 to 6.0 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.3 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0.2 to 0.4 | |
| 0 to 0.030 |