ACI-ASTM CA40F Steel vs. EN 1.4806 Stainless Steel
Both ACI-ASTM CA40F steel and EN 1.4806 stainless steel are iron alloys. They have 60% of their average alloy composition in common.
For each property being compared, the top bar is ACI-ASTM CA40F steel and the bottom bar is EN 1.4806 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 230 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 13 | |
| 6.8 |
| Fatigue Strength, MPa | 320 | |
| 120 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 76 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 550 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 320 |
| Maximum Temperature: Corrosion, °C | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 750 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1380 |
| Melting Onset (Solidus), °C | 1390 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 27 | |
| 12 |
| Thermal Expansion, µm/m-K | 10 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.0 | |
| 1.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.5 | |
| 1.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.5 | |
| 31 |
| Density, g/cm3 | 7.7 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 5.4 |
| Embodied Energy, MJ/kg | 28 | |
| 76 |
| Embodied Water, L/kg | 100 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 14 | |
| 18 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 | |
| 27 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 790 | |
| 160 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 16 |
| Strength to Weight: Bending, points | 24 | |
| 17 |
| Thermal Diffusivity, mm2/s | 7.2 | |
| 3.1 |
| Thermal Shock Resistance, points | 28 | |
| 11 |
Alloy Composition
| Carbon (C), % | 0.2 to 0.4 | |
| 0.3 to 0.5 |
| Chromium (Cr), % | 11.5 to 14 | |
| 16 to 18 |
| Iron (Fe), % | 81.6 to 88.3 | |
| 40.4 to 48.7 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.5 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 1.0 | |
| 34 to 36 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.5 | |
| 1.0 to 2.5 |
| Sulfur (S), % | 0.2 to 0.4 | |
| 0 to 0.030 |