ACI-ASTM CA6N Steel vs. ASTM Grade LC3 Steel
Both ACI-ASTM CA6N steel and ASTM grade LC3 steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CA6N steel and the bottom bar is ASTM grade LC3 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 | |
| 27 |
| Fatigue Strength, MPa | 640 | |
| 230 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Reduction in Area, % | 57 | |
| 40 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1080 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 1060 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 740 | |
| 410 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 23 | |
| 52 |
| Thermal Expansion, µm/m-K | 9.9 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.6 | |
| 7.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.0 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 4.0 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.5 | |
| 1.7 |
| Embodied Energy, MJ/kg | 35 | |
| 23 |
| Embodied Water, L/kg | 110 | |
| 52 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2900 | |
| 260 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 38 | |
| 20 |
| Strength to Weight: Bending, points | 30 | |
| 19 |
| Thermal Diffusivity, mm2/s | 6.1 | |
| 14 |
| Thermal Shock Resistance, points | 40 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0 to 0.15 |
| Chromium (Cr), % | 10.5 to 12.5 | |
| 0 |
| Iron (Fe), % | 77.9 to 83.5 | |
| 94.4 to 96.5 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.5 to 0.8 |
| Nickel (Ni), % | 6.0 to 8.0 | |
| 3.0 to 4.0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.045 |