ACI-ASTM CA6N Steel vs. EN 1.8918 Steel

Both ACI-ASTM CA6N steel and EN 1.8918 steel are iron alloys. They have 82% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA6N steel and the bottom bar is EN 1.8918 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
19
Fatigue Strength, MPa 640
330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 1080
640
Tensile Strength: Yield (Proof), MPa 1060
490

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 740
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 23
46
Thermal Expansion, µm/m-K 9.9
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.6
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 11
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.7
Embodied Energy, MJ/kg 35
24
Embodied Water, L/kg 110
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110
Resilience: Unit (Modulus of Resilience), kJ/m3 2900
640
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 38
23
Strength to Weight: Bending, points 30
21
Thermal Diffusivity, mm2/s 6.1
12
Thermal Shock Resistance, points 40
19

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.050
Carbon (C), % 0 to 0.060
0 to 0.2
Chromium (Cr), % 10.5 to 12.5
0 to 0.3
Copper (Cu), % 0
0 to 0.7
Iron (Fe), % 77.9 to 83.5
95.2 to 98.9
Manganese (Mn), % 0 to 0.5
1.1 to 1.7
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 6.0 to 8.0
0 to 0.8
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.025
Phosphorus (P), % 0 to 0.020
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.020
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.2