ACI-ASTM CA6NM Steel vs. EN 1.4951 Stainless Steel

Both ACI-ASTM CA6NM steel and EN 1.4951 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CA6NM steel and the bottom bar is EN 1.4951 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250
170
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
38
Fatigue Strength, MPa 380
190
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 850
630
Tensile Strength: Yield (Proof), MPa 620
220

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 770
1100
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
25
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.5
4.3
Embodied Energy, MJ/kg 34
61
Embodied Water, L/kg 110
190

Common Calculations

PREN (Pitting Resistance) 15
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
190
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
22
Strength to Weight: Bending, points 26
21
Thermal Diffusivity, mm2/s 6.7
3.9
Thermal Shock Resistance, points 31
14

Alloy Composition

Carbon (C), % 0 to 0.060
0.040 to 0.080
Chromium (Cr), % 11.5 to 14
24 to 26
Iron (Fe), % 78.4 to 84.6
49.1 to 57
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.4 to 1.0
0
Nickel (Ni), % 3.5 to 4.5
19 to 22
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.015