ACI-ASTM CB30 Steel vs. EN 1.4315 Stainless Steel

Both ACI-ASTM CB30 steel and EN 1.4315 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB30 steel and the bottom bar is EN 1.4315 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 500
630
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 940
960
Melting Completion (Liquidus), °C 1430
1420
Melting Onset (Solidus), °C 1380
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
15
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 10
15
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.3
3.0
Embodied Energy, MJ/kg 33
43
Embodied Water, L/kg 130
150

Common Calculations

PREN (Pitting Resistance) 20
22
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 5.6
4.0
Thermal Shock Resistance, points 17
14

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.060
Chromium (Cr), % 18 to 21
18 to 20
Copper (Cu), % 0 to 1.2
0
Iron (Fe), % 72.9 to 82
65.7 to 73.9
Manganese (Mn), % 0 to 1.0
0 to 2.0
Nickel (Ni), % 0 to 2.0
8.0 to 11
Nitrogen (N), % 0
0.12 to 0.22
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015