MakeItFrom.com
Menu (ESC)

ACI-ASTM CB30 Steel vs. S41003 Stainless Steel

Both ACI-ASTM CB30 steel and S41003 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CB30 steel and the bottom bar is S41003 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 500
520
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 290
270
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 940
720
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 21
27
Thermal Expansion, µm/m-K 11
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 3.0
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 10
7.0
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.9
Embodied Energy, MJ/kg 33
27
Embodied Water, L/kg 130
97

Common Calculations

PREN (Pitting Resistance) 20
12
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
18
Thermal Diffusivity, mm2/s 5.6
7.2
Thermal Shock Resistance, points 17
19

Alloy Composition

Carbon (C), % 0 to 0.3
0 to 0.030
Chromium (Cr), % 18 to 21
10.5 to 12.5
Copper (Cu), % 0 to 1.2
0
Iron (Fe), % 72.9 to 82
83.4 to 89.5
Manganese (Mn), % 0 to 1.0
0 to 1.5
Nickel (Ni), % 0 to 2.0
0 to 1.5
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030