ACI-ASTM CC50 Steel vs. AWS E309

Both ACI-ASTM CC50 steel and AWS E309 are iron alloys. They have 87% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CC50 steel and the bottom bar is AWS E309.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Poisson's Ratio 0.27
0.27
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 430
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 490
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 11
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 14
20
Density, g/cm3 7.6
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.7
Embodied Energy, MJ/kg 39
52
Embodied Water, L/kg 170
180

Common Calculations

PREN (Pitting Resistance) 28
25
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 16
22
Strength to Weight: Bending, points 17
21
Thermal Diffusivity, mm2/s 4.5
4.0
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.5
0 to 0.15
Chromium (Cr), % 26 to 30
22 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 62.9 to 74
55.8 to 65.5
Manganese (Mn), % 0 to 1.0
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0 to 4.0
12 to 14
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030