ACI-ASTM CD6MN Steel vs. C82000 Copper

ACI-ASTM CD6MN steel belongs to the iron alloys classification, while C82000 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CD6MN steel and the bottom bar is C82000 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 28
8.0 to 20
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 80
45
Tensile Strength: Ultimate (UTS), MPa 730
350 to 690
Tensile Strength: Yield (Proof), MPa 510
140 to 520

Thermal Properties

Latent Heat of Fusion, J/g 300
220
Maximum Temperature: Mechanical, °C 1100
220
Melting Completion (Liquidus), °C 1440
1090
Melting Onset (Solidus), °C 1390
970
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
260
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
45
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
46

Otherwise Unclassified Properties

Base Metal Price, % relative 17
60
Density, g/cm3 7.7
8.9
Embodied Carbon, kg CO2/kg material 3.4
5.0
Embodied Energy, MJ/kg 48
77
Embodied Water, L/kg 170
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
51 to 55
Resilience: Unit (Modulus of Resilience), kJ/m3 650
80 to 1120
Stiffness to Weight: Axial, points 15
7.5
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 26
11 to 22
Strength to Weight: Bending, points 23
12 to 20
Thermal Diffusivity, mm2/s 4.4
76
Thermal Shock Resistance, points 20
12 to 24

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Beryllium (Be), % 0
0.45 to 0.8
Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 24 to 27
0 to 0.1
Cobalt (Co), % 0
2.2 to 2.7
Copper (Cu), % 0
95.2 to 97.4
Iron (Fe), % 62.1 to 70.1
0 to 0.1
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 1.8 to 2.5
0
Nickel (Ni), % 4.0 to 6.0
0 to 0.2
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.15
Sulfur (S), % 0 to 0.040
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.5