ACI-ASTM CE30 Steel vs. EN 1.5520 Steel

Both ACI-ASTM CE30 steel and EN 1.5520 steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CE30 steel and the bottom bar is EN 1.5520 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
120 to 170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
11 to 21
Fatigue Strength, MPa 170
210 to 300
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 630
410 to 1410
Tensile Strength: Yield (Proof), MPa 310
300 to 480

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
50
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.4
Embodied Energy, MJ/kg 49
19
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
42 to 230
Resilience: Unit (Modulus of Resilience), kJ/m3 240
240 to 600
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
15 to 50
Strength to Weight: Bending, points 21
16 to 36
Thermal Diffusivity, mm2/s 3.6
13
Thermal Shock Resistance, points 13
12 to 41

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.3
0.15 to 0.2
Chromium (Cr), % 26 to 30
0 to 0.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 55.1 to 66
97.7 to 98.9
Manganese (Mn), % 0 to 1.5
0.9 to 1.2
Nickel (Ni), % 8.0 to 11
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 2.0
0 to 0.3
Sulfur (S), % 0 to 0.040
0 to 0.025