ACI-ASTM CE30 Steel vs. EN 1.6220 Steel

Both ACI-ASTM CE30 steel and EN 1.6220 steel are iron alloys. They have 62% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CE30 steel and the bottom bar is EN 1.6220 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11
23 to 25
Fatigue Strength, MPa 170
240 to 250
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 630
550 to 580
Tensile Strength: Yield (Proof), MPa 310
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
52
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 19
2.1
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.4
1.5
Embodied Energy, MJ/kg 49
19
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 240
300 to 310
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
19 to 20
Strength to Weight: Bending, points 21
19 to 20
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 13
16 to 17

Alloy Composition

Carbon (C), % 0 to 0.3
0.17 to 0.23
Chromium (Cr), % 26 to 30
0
Iron (Fe), % 55.1 to 66
96.7 to 98.8
Manganese (Mn), % 0 to 1.5
1.0 to 1.6
Nickel (Ni), % 8.0 to 11
0 to 0.8
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030