ACI-ASTM CE30 Steel vs. SAE-AISI O7 Steel

Both ACI-ASTM CE30 steel and SAE-AISI O7 steel are iron alloys. They have 62% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CE30 steel and the bottom bar is SAE-AISI O7 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 630
680 to 2110

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1410
1480
Melting Onset (Solidus), °C 1360
1430
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 14
41
Thermal Expansion, µm/m-K 17
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 19
6.0
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.4
2.3
Embodied Energy, MJ/kg 49
33
Embodied Water, L/kg 180
52

Common Calculations

PREN (Pitting Resistance) 28
3.6
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
24 to 74
Strength to Weight: Bending, points 21
22 to 46
Thermal Diffusivity, mm2/s 3.6
11
Thermal Shock Resistance, points 13
23 to 70

Alloy Composition

Carbon (C), % 0 to 0.3
1.1 to 1.3
Chromium (Cr), % 26 to 30
0.35 to 0.85
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 55.1 to 66
92.9 to 97.6
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.3
Nickel (Ni), % 8.0 to 11
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030
Tungsten (W), % 0
1.0 to 2.0
Vanadium (V), % 0
0 to 0.4