ACI-ASTM CF16F Steel vs. EN 1.4405 Stainless Steel

Both ACI-ASTM CF16F steel and EN 1.4405 stainless steel are iron alloys. They have 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF16F steel and the bottom bar is EN 1.4405 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 50
17
Fatigue Strength, MPa 270
370
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 530
860
Tensile Strength: Yield (Proof), MPa 280
610

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 980
870
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
17
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 18
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.4
2.8
Embodied Energy, MJ/kg 47
39
Embodied Water, L/kg 150
130

Common Calculations

PREN (Pitting Resistance) 22
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
130
Resilience: Unit (Modulus of Resilience), kJ/m3 190
950
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
31
Strength to Weight: Bending, points 19
26
Thermal Diffusivity, mm2/s 4.3
4.6
Thermal Shock Resistance, points 12
29

Alloy Composition

Carbon (C), % 0 to 0.16
0 to 0.060
Chromium (Cr), % 18 to 21
15 to 17
Iron (Fe), % 61.3 to 72.8
73.6 to 80.3
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0 to 1.5
0.7 to 1.5
Nickel (Ni), % 9.0 to 12
4.0 to 6.0
Phosphorus (P), % 0 to 0.17
0 to 0.035
Selenium (Se), % 0.2 to 0.35
0
Silicon (Si), % 0 to 2.0
0 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.025