ACI-ASTM CF20 Steel vs. AWS E320

Both ACI-ASTM CF20 steel and AWS E320 are iron alloys. They have 68% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF20 steel and the bottom bar is AWS E320.

ACI-ASTM CF20 (SCS12, J92602) Cast Stainless Steel AWS E320 (W88021) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		50
Elongation at Break, %		34

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		77
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		530
Tensile Strength: Ultimate (UTS), MPa		620

Thermal Properties

Latent Heat of Fusion, J/g		300
Latent Heat of Fusion, J/g		300

Melting Completion (Liquidus), °C		1420
Melting Completion (Liquidus), °C		1410

Melting Onset (Solidus), °C		1410
Melting Onset (Solidus), °C		1360

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		460

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		14

Otherwise Unclassified Properties

Base Metal Price, % relative		16
Base Metal Price, % relative		38

Density, g/cm³		7.8
Density, g/cm³		8.2

Embodied Carbon, kg CO₂/kg material		3.1
Embodied Carbon, kg CO₂/kg material		6.5

Embodied Energy, MJ/kg		44
Embodied Energy, MJ/kg		91

Embodied Water, L/kg		150
Embodied Water, L/kg		220

Common Calculations

PREN (Pitting Resistance)		20
PREN (Pitting Resistance)		28

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		19
Strength to Weight: Axial, points		21

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		20

Thermal Shock Resistance, points		11
Thermal Shock Resistance, points		16

Alloy Composition

Carbon (C), %		0 to 0.2
Carbon (C), %		0 to 0.070

Chromium (Cr), %		18 to 21
Chromium (Cr), %		19 to 21

Copper (Cu), %		0
Copper (Cu), %		3.0 to 4.0

Iron (Fe), %		64.2 to 74
Iron (Fe), %		31.8 to 43.5

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		0.5 to 2.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		2.0 to 3.0

Nickel (Ni), %		8.0 to 11
Nickel (Ni), %		32 to 36

Niobium (Nb), %		0
Niobium (Nb), %		0 to 1.0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 2.0
Silicon (Si), %		0 to 0.6

Sulfur (S), %		0 to 0.040
Sulfur (S), %		0 to 0.030