ACI-ASTM CF3 Steel vs. EN 1.4438 Stainless Steel

Both ACI-ASTM CF3 steel and EN 1.4438 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3 steel and the bottom bar is EN 1.4438 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 60
41
Fatigue Strength, MPa 270
220
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
79
Tensile Strength: Ultimate (UTS), MPa 510
620
Tensile Strength: Yield (Proof), MPa 250
250

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 420
420
Maximum Temperature: Mechanical, °C 960
1000
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1450
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
14
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 16
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.2
4.4
Embodied Energy, MJ/kg 45
60
Embodied Water, L/kg 150
160

Common Calculations

PREN (Pitting Resistance) 20
31
Resilience: Ultimate (Unit Rupture Work), MJ/m3 250
200
Resilience: Unit (Modulus of Resilience), kJ/m3 160
150
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 4.3
3.7
Thermal Shock Resistance, points 11
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 17 to 21
17.5 to 19.5
Iron (Fe), % 62.9 to 75
57.3 to 66.5
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.5
3.0 to 4.0
Nickel (Ni), % 8.0 to 12
13 to 16
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 2.0
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015