ACI-ASTM CF3MN Steel vs. EN 1.4460 Stainless Steel

Both ACI-ASTM CF3MN steel and EN 1.4460 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF3MN steel and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
220
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 39
21
Fatigue Strength, MPa 250
330
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 580
750
Tensile Strength: Yield (Proof), MPa 290
510

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
450
Maximum Temperature: Mechanical, °C 1010
1100
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
18
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.9
3.4
Embodied Energy, MJ/kg 53
48
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 30
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
140
Resilience: Unit (Modulus of Resilience), kJ/m3 210
640
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
27
Strength to Weight: Bending, points 20
24
Thermal Diffusivity, mm2/s 4.1
4.0
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 17 to 22
25 to 28
Iron (Fe), % 58.7 to 71.9
60.2 to 69.2
Manganese (Mn), % 0 to 1.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
1.3 to 2.0
Nickel (Ni), % 9.0 to 13
4.5 to 6.5
Nitrogen (N), % 0.1 to 0.2
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015