ACI-ASTM CF8M Steel vs. ASTM A356 Grade 1

Both ACI-ASTM CF8M steel and ASTM A356 grade 1 are iron alloys. Both are furnished in the heat treated (HT) condition. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF8M steel and the bottom bar is ASTM A356 grade 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 50
23
Fatigue Strength, MPa 280
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 540
550
Tensile Strength: Yield (Proof), MPa 290
280

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
1.4
Embodied Energy, MJ/kg 53
18
Embodied Water, L/kg 160
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
210
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 12
18

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.35
Chromium (Cr), % 18 to 21
0
Iron (Fe), % 60.3 to 71
98.3 to 100
Manganese (Mn), % 0 to 1.5
0 to 0.7
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0 to 0.6
Sulfur (S), % 0 to 0.040
0 to 0.030