ACI-ASTM CF8M Steel vs. EN 1.0454 Cast Steel

Both ACI-ASTM CF8M steel and EN 1.0454 cast steel are iron alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CF8M steel and the bottom bar is EN 1.0454 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 50
25
Fatigue Strength, MPa 280
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 540
550
Tensile Strength: Yield (Proof), MPa 290
300

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1400
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
53
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.8
1.4
Embodied Energy, MJ/kg 53
18
Embodied Water, L/kg 160
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
110
Resilience: Unit (Modulus of Resilience), kJ/m3 210
240
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 4.3
14
Thermal Shock Resistance, points 12
17

Alloy Composition

Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 18 to 21
0
Iron (Fe), % 60.3 to 71
99.935 to 100
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 9.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 2.0
0
Sulfur (S), % 0 to 0.040
0 to 0.030