ACI-ASTM CG12 Steel vs. EN 1.3555 Steel
Both ACI-ASTM CG12 steel and EN 1.3555 steel are iron alloys. They have 73% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CG12 steel and the bottom bar is EN 1.3555 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 | |
| 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 770 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 1040 | |
| 540 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1500 |
| Melting Onset (Solidus), °C | 1370 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 9.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.3 | |
| 5.6 |
| Embodied Energy, MJ/kg | 48 | |
| 81 |
| Embodied Water, L/kg | 160 | |
| 90 |
Common Calculations
| PREN (Pitting Resistance) | 22 | |
| 18 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 27 |
| Strength to Weight: Bending, points | 19 | |
| 23 |
| Thermal Shock Resistance, points | 12 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 20 to 23 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 60.3 to 70 | |
| 85.4 to 87.7 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.15 to 0.35 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 4.5 |
| Nickel (Ni), % | 10 to 13 | |
| 3.2 to 3.6 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 2.0 | |
| 0.1 to 0.25 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.15 |
| Vanadium (V), % | 0 | |
| 1.0 to 1.3 |