ACI-ASTM CG6MMN Steel vs. EN 1.1060 Steel
Both ACI-ASTM CG6MMN steel and EN 1.1060 steel are iron alloys. They have 58% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CG6MMN steel and the bottom bar is EN 1.1060 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 490 to 1720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1080 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1380 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 17 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 22 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 68 | |
| 18 |
| Embodied Water, L/kg | 180 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 17 to 61 |
| Strength to Weight: Bending, points | 22 | |
| 18 to 41 |
| Thermal Shock Resistance, points | 14 | |
| 16 to 55 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0.32 to 0.39 |
| Chromium (Cr), % | 20.5 to 23.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 51.9 to 62.1 | |
| 98.2 to 99.16 |
| Manganese (Mn), % | 4.0 to 6.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 11.5 to 13.5 | |
| 0 |
| Niobium (Nb), % | 0.1 to 0.3 | |
| 0 |
| Nitrogen (N), % | 0.2 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.020 to 0.035 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |