ACI-ASTM CG6MMN Steel vs. EN 1.5402 Steel

Both ACI-ASTM CG6MMN steel and EN 1.5402 steel are iron alloys. They have 59% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CG6MMN steel and the bottom bar is EN 1.5402 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
23
Fatigue Strength, MPa 260
260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 670
580
Tensile Strength: Yield (Proof), MPa 320
370

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1080
410
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 22
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.8
1.7
Embodied Energy, MJ/kg 68
22
Embodied Water, L/kg 180
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
120
Resilience: Unit (Modulus of Resilience), kJ/m3 260
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 22
20
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.18
Chromium (Cr), % 20.5 to 23.5
0
Iron (Fe), % 51.9 to 62.1
97.3 to 98.7
Manganese (Mn), % 4.0 to 6.0
0.9 to 1.4
Molybdenum (Mo), % 1.5 to 3.0
0.4 to 0.6
Nickel (Ni), % 11.5 to 13.5
0
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0.1 to 0.3
0.040 to 0.080