ACI-ASTM CG6MMN Steel vs. SAE-AISI 1017 Steel

Both ACI-ASTM CG6MMN steel and SAE-AISI 1017 steel are iron alloys. They have 58% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CG6MMN steel and the bottom bar is SAE-AISI 1017 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
120 to 130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
20 to 30
Fatigue Strength, MPa 260
170 to 270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 670
420 to 460
Tensile Strength: Yield (Proof), MPa 320
220 to 390

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1080
400
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 17
12

Otherwise Unclassified Properties

Base Metal Price, % relative 22
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.8
1.4
Embodied Energy, MJ/kg 68
18
Embodied Water, L/kg 180
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
88 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
130 to 400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
15 to 16
Strength to Weight: Bending, points 22
16 to 17
Thermal Shock Resistance, points 14
13 to 14

Alloy Composition

Carbon (C), % 0 to 0.060
0.15 to 0.2
Chromium (Cr), % 20.5 to 23.5
0
Iron (Fe), % 51.9 to 62.1
99.11 to 99.55
Manganese (Mn), % 4.0 to 6.0
0.3 to 0.6
Molybdenum (Mo), % 1.5 to 3.0
0
Nickel (Ni), % 11.5 to 13.5
0
Niobium (Nb), % 0.1 to 0.3
0
Nitrogen (N), % 0.2 to 0.4
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050
Vanadium (V), % 0.1 to 0.3
0