ACI-ASTM CH10 Steel vs. C10500 Copper
ACI-ASTM CH10 steel belongs to the iron alloys classification, while C10500 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CH10 steel and the bottom bar is C10500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
120 |
Elongation at Break, % | 34 | |
2.8 to 51 |
Poisson's Ratio | 0.27 | |
0.34 |
Shear Modulus, GPa | 78 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 540 | |
220 to 400 |
Tensile Strength: Yield (Proof), MPa | 230 | |
75 to 400 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
210 |
Maximum Temperature: Mechanical, °C | 1100 | |
200 |
Melting Completion (Liquidus), °C | 1410 | |
1080 |
Melting Onset (Solidus), °C | 1370 | |
1080 |
Specific Heat Capacity, J/kg-K | 480 | |
390 |
Thermal Conductivity, W/m-K | 15 | |
390 |
Thermal Expansion, µm/m-K | 16 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
100 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
100 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 20 | |
32 |
Density, g/cm3 | 7.8 | |
9.0 |
Embodied Carbon, kg CO2/kg material | 3.7 | |
2.6 |
Embodied Energy, MJ/kg | 53 | |
42 |
Embodied Water, L/kg | 180 | |
350 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
11 to 90 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
24 to 680 |
Stiffness to Weight: Axial, points | 14 | |
7.2 |
Stiffness to Weight: Bending, points | 25 | |
18 |
Strength to Weight: Axial, points | 19 | |
6.8 to 12 |
Strength to Weight: Bending, points | 19 | |
9.1 to 14 |
Thermal Diffusivity, mm2/s | 3.9 | |
110 |
Thermal Shock Resistance, points | 12 | |
7.8 to 14 |
Alloy Composition
Carbon (C), % | 0 to 0.1 | |
0 |
Chromium (Cr), % | 22 to 26 | |
0 |
Copper (Cu), % | 0 | |
99.89 to 99.966 |
Iron (Fe), % | 54.8 to 66 | |
0 |
Manganese (Mn), % | 0 to 1.5 | |
0 |
Molybdenum (Mo), % | 0 to 0.5 | |
0 |
Nickel (Ni), % | 12 to 15 | |
0 |
Oxygen (O), % | 0 | |
0 to 0.0010 |
Phosphorus (P), % | 0 to 0.040 | |
0 |
Silicon (Si), % | 0 to 2.0 | |
0 |
Silver (Ag), % | 0 | |
0.034 to 0.060 |
Sulfur (S), % | 0 to 0.040 | |
0 |
Residuals, % | 0 | |
0 to 0.050 |