ACI-ASTM CH10 Steel vs. S24000 Stainless Steel

Both ACI-ASTM CH10 steel and S24000 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CH10 steel and the bottom bar is S24000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
210
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
39
Fatigue Strength, MPa 180
370
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 540
770
Tensile Strength: Yield (Proof), MPa 230
430

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 440
410
Maximum Temperature: Mechanical, °C 1100
910
Melting Completion (Liquidus), °C 1410
1390
Melting Onset (Solidus), °C 1370
1350
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 20
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 3.7
2.7
Embodied Energy, MJ/kg 53
39
Embodied Water, L/kg 180
150

Common Calculations

PREN (Pitting Resistance) 25
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
260
Resilience: Unit (Modulus of Resilience), kJ/m3 140
470
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 19
28
Strength to Weight: Bending, points 19
24
Thermal Shock Resistance, points 12
16

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.080
Chromium (Cr), % 22 to 26
17 to 19
Iron (Fe), % 54.8 to 66
61.5 to 69
Manganese (Mn), % 0 to 1.5
11.5 to 14.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 12 to 15
2.3 to 3.7
Nitrogen (N), % 0
0.2 to 0.4
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0 to 2.0
0 to 0.75
Sulfur (S), % 0 to 0.040
0 to 0.030