ACI-ASTM CK20 Steel vs. Grade CY40 Nickel

ACI-ASTM CK20 steel belongs to the iron alloys classification, while grade CY40 nickel belongs to the nickel alloys. They have 43% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK20 steel and the bottom bar is grade CY40 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 37
34
Fatigue Strength, MPa 220
160
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Tensile Strength: Ultimate (UTS), MPa 530
540
Tensile Strength: Yield (Proof), MPa 260
220

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1400
1350
Melting Onset (Solidus), °C 1430
1300
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
14
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 25
55
Density, g/cm3 7.8
8.4
Embodied Carbon, kg CO2/kg material 4.4
9.1
Embodied Energy, MJ/kg 62
130
Embodied Water, L/kg 190
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
150
Resilience: Unit (Modulus of Resilience), kJ/m3 170
130
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 3.7
3.7
Thermal Shock Resistance, points 13
16

Alloy Composition

Carbon (C), % 0 to 0.2
0 to 0.4
Chromium (Cr), % 23 to 27
14 to 17
Iron (Fe), % 46.7 to 58
0 to 11
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 0 to 0.5
0
Nickel (Ni), % 19 to 22
67 to 86
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 2.0
0 to 3.0
Sulfur (S), % 0 to 0.040
0 to 0.030