ACI-ASTM CK35MN Steel vs. SAE-AISI 1025 Steel

Both ACI-ASTM CK35MN steel and SAE-AISI 1025 steel are iron alloys. They have 48% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CK35MN steel and the bottom bar is SAE-AISI 1025 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
130 to 140
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 40
17 to 28
Fatigue Strength, MPa 270
190 to 280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 650
450 to 500
Tensile Strength: Yield (Proof), MPa 310
250 to 420

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
1.8
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.9
1.4
Embodied Energy, MJ/kg 81
18
Embodied Water, L/kg 210
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
80 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 240
170 to 470
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
16 to 18
Strength to Weight: Bending, points 21
17 to 18
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 14
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.035
0.22 to 0.28
Chromium (Cr), % 22 to 24
0
Copper (Cu), % 0 to 0.4
0
Iron (Fe), % 43.4 to 51.8
99.03 to 99.48
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 6.0 to 6.8
0
Nickel (Ni), % 20 to 22
0
Nitrogen (N), % 0.21 to 0.32
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.020
0 to 0.050