ACI-ASTM CN3M Steel vs. R60802 Alloy

ACI-ASTM CN3M steel belongs to the iron alloys classification, while R60802 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ACI-ASTM CN3M steel and the bottom bar is R60802 alloy.

ACI-ASTM CN3M (J94652) Cast Stainless Steel UNS R60802 Zirconium-Tin Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		98

Elongation at Break, %		34
Elongation at Break, %		22

Poisson's Ratio		0.28
Poisson's Ratio		0.34

Shear Modulus, GPa		80
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		500
Tensile Strength: Ultimate (UTS), MPa		430

Tensile Strength: Yield (Proof), MPa		190
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		250

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		270

Thermal Conductivity, W/m-K		13
Thermal Conductivity, W/m-K		22

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		6.0

Otherwise Unclassified Properties

Density, g/cm³		8.1
Density, g/cm³		6.5

Embodied Water, L/kg		200
Embodied Water, L/kg		290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		130
Resilience: Ultimate (Unit Rupture Work), MJ/m³		85

Resilience: Unit (Modulus of Resilience), kJ/m³		89
Resilience: Unit (Modulus of Resilience), kJ/m³		380

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		8.3

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		17
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		17
Strength to Weight: Bending, points		19

Thermal Diffusivity, mm²/s		3.4
Thermal Diffusivity, mm²/s		12

Thermal Shock Resistance, points		11
Thermal Shock Resistance, points		53

Alloy Composition

Carbon (C), %		0 to 0.030
Carbon (C), %		0

Chromium (Cr), %		20 to 22
Chromium (Cr), %		0.050 to 0.15

Iron (Fe), %		42.4 to 52.5
Iron (Fe), %		0.070 to 0.2

Manganese (Mn), %		0 to 2.0
Manganese (Mn), %		0

Molybdenum (Mo), %		4.5 to 5.5
Molybdenum (Mo), %		0

Nickel (Ni), %		23 to 27
Nickel (Ni), %		0.030 to 0.080

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		1.2 to 1.7

Zirconium (Zr), %		0
Zirconium (Zr), %		97.8 to 98.7

Residuals, %		0
Residuals, %		0 to 0.11