ACI-ASTM CN7MS Steel vs. ASTM A387 Grade 21L Class 1
Both ACI-ASTM CN7MS steel and ASTM A387 grade 21L class 1 are iron alloys. They have 54% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CN7MS steel and the bottom bar is ASTM A387 grade 21L class 1.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 | |
| 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 39 | |
| 21 |
| Fatigue Strength, MPa | 200 | |
| 160 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 500 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 1040 | |
| 480 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1470 |
| Melting Onset (Solidus), °C | 1350 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 41 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 4.1 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 1.8 |
| Embodied Energy, MJ/kg | 71 | |
| 23 |
| Embodied Water, L/kg | 180 | |
| 62 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 6.4 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 84 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 140 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 18 |
| Strength to Weight: Bending, points | 19 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 11 |
| Thermal Shock Resistance, points | 13 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.1 |
| Chromium (Cr), % | 18 to 20 | |
| 2.8 to 3.3 |
| Copper (Cu), % | 1.5 to 2.0 | |
| 0 |
| Iron (Fe), % | 45.4 to 53.5 | |
| 94.4 to 96.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 2.5 to 3.0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 22 to 25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 2.5 to 3.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |