ACI-ASTM CN7MS Steel vs. EN 1.7366 Steel
Both ACI-ASTM CN7MS steel and EN 1.7366 steel are iron alloys. They have 56% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CN7MS steel and the bottom bar is EN 1.7366 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 | |
| 140 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 39 | |
| 17 to 19 |
| Fatigue Strength, MPa | 200 | |
| 160 to 320 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 460 to 710 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 230 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 1040 | |
| 510 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1460 |
| Melting Onset (Solidus), °C | 1350 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 40 |
| Thermal Expansion, µm/m-K | 16 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 4.3 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 1.7 |
| Embodied Energy, MJ/kg | 71 | |
| 23 |
| Embodied Water, L/kg | 180 | |
| 69 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 6.8 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 74 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 140 to 600 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 19 | |
| 16 to 25 |
| Strength to Weight: Bending, points | 19 | |
| 17 to 23 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 11 |
| Thermal Shock Resistance, points | 13 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.18 |
| Chromium (Cr), % | 18 to 20 | |
| 4.0 to 6.0 |
| Copper (Cu), % | 1.5 to 2.0 | |
| 0 |
| Iron (Fe), % | 45.4 to 53.5 | |
| 91.9 to 95.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 2.5 to 3.0 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 22 to 25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 2.5 to 3.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |