ACI-ASTM CN7MS Steel vs. C64210 Bronze
ACI-ASTM CN7MS steel belongs to the iron alloys classification, while C64210 bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is ACI-ASTM CN7MS steel and the bottom bar is C64210 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 39 | |
| 35 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 77 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 570 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1040 | |
| 210 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1040 |
| Melting Onset (Solidus), °C | 1350 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 430 |
| Thermal Conductivity, W/m-K | 12 | |
| 48 |
| Thermal Expansion, µm/m-K | 16 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 3.0 |
| Embodied Energy, MJ/kg | 71 | |
| 49 |
| Embodied Water, L/kg | 180 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 360 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 19 | |
| 19 |
| Strength to Weight: Bending, points | 19 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 13 |
| Thermal Shock Resistance, points | 13 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 6.3 to 7.0 |
| Arsenic (As), % | 0 | |
| 0 to 0.15 |
| Carbon (C), % | 0 to 0.070 | |
| 0 |
| Chromium (Cr), % | 18 to 20 | |
| 0 |
| Copper (Cu), % | 1.5 to 2.0 | |
| 89 to 92.2 |
| Iron (Fe), % | 45.4 to 53.5 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 2.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 22 to 25 | |
| 0 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 2.5 to 3.5 | |
| 1.5 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |