MakeItFrom.com
Menu (ESC)

AISI 201 Stainless Steel vs. AWS E80C-B8

Both AISI 201 stainless steel and AWS E80C-B8 are iron alloys. They have 82% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AISI 201 stainless steel and the bottom bar is AWS E80C-B8.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 4.6 to 51
19
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 650 to 1450
620
Tensile Strength: Yield (Proof), MPa 300 to 1080
540

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Melting Completion (Liquidus), °C 1410
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
9.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
11

Otherwise Unclassified Properties

Base Metal Price, % relative 12
6.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.6
2.1
Embodied Energy, MJ/kg 38
28
Embodied Water, L/kg 140
89

Common Calculations

PREN (Pitting Resistance) 19
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 61 to 340
110
Resilience: Unit (Modulus of Resilience), kJ/m3 230 to 2970
740
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23 to 52
22
Strength to Weight: Bending, points 22 to 37
21
Thermal Diffusivity, mm2/s 4.0
6.9
Thermal Shock Resistance, points 14 to 32
17

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 16 to 18
8.0 to 10.5
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 67.5 to 75
85.5 to 90.6
Manganese (Mn), % 5.5 to 7.5
0.4 to 1.0
Molybdenum (Mo), % 0
0.8 to 1.2
Nickel (Ni), % 3.5 to 5.5
0 to 0.2
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.060
0 to 0.025
Silicon (Si), % 0 to 1.0
0.25 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5