AISI 201 Stainless Steel vs. Solder Alloy 402

AISI 201 stainless steel belongs to the iron alloys classification, while solder alloy 402 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI 201 stainless steel and the bottom bar is solder alloy 402.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
52
Elongation at Break, % 4.6 to 51
20
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 77
19
Tensile Strength: Ultimate (UTS), MPa 650 to 1450
57

Thermal Properties

Latent Heat of Fusion, J/g 280
64
Melting Completion (Liquidus), °C 1410
310
Melting Onset (Solidus), °C 1370
230
Specific Heat Capacity, J/kg-K 480
230
Thermal Conductivity, W/m-K 15
61
Thermal Expansion, µm/m-K 17
22

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
18

Otherwise Unclassified Properties

Density, g/cm3 7.7
7.3
Embodied Carbon, kg CO2/kg material 2.6
15
Embodied Energy, MJ/kg 38
250
Embodied Water, L/kg 140
1180

Common Calculations

Stiffness to Weight: Axial, points 14
3.9
Stiffness to Weight: Bending, points 25
17
Strength to Weight: Axial, points 23 to 52
2.2
Strength to Weight: Bending, points 22 to 37
4.5
Thermal Diffusivity, mm2/s 4.0
37
Thermal Shock Resistance, points 14 to 32
3.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.1
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.15
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
2.5 to 3.5
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 67.5 to 75
0 to 0.020
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 5.5 to 7.5
0
Nickel (Ni), % 3.5 to 5.5
0 to 0.010
Nitrogen (N), % 0 to 0.25
0
Phosphorus (P), % 0 to 0.060
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
95.9 to 97.5
Zinc (Zn), % 0
0 to 0.0010