AISI 201L Stainless Steel vs. 6070 Aluminum
AISI 201L stainless steel belongs to the iron alloys classification, while 6070 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AISI 201L stainless steel and the bottom bar is 6070 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 70 |
| Elongation at Break, % | 22 to 46 | |
| 5.6 to 8.6 |
| Fatigue Strength, MPa | 270 to 530 | |
| 95 to 130 |
| Poisson's Ratio | 0.28 | |
| 0.33 |
| Shear Modulus, GPa | 77 | |
| 26 |
| Shear Strength, MPa | 520 to 660 | |
| 220 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 1040 | |
| 370 to 380 |
| Tensile Strength: Yield (Proof), MPa | 290 to 790 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 160 |
| Melting Completion (Liquidus), °C | 1410 | |
| 650 |
| Melting Onset (Solidus), °C | 1370 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 900 |
| Thermal Conductivity, W/m-K | 15 | |
| 160 |
| Thermal Expansion, µm/m-K | 17 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 7.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 8.3 |
| Embodied Energy, MJ/kg | 38 | |
| 150 |
| Embodied Water, L/kg | 140 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 20 to 32 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 1570 | |
| 880 to 900 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 50 |
| Strength to Weight: Axial, points | 27 to 37 | |
| 38 |
| Strength to Weight: Bending, points | 24 to 30 | |
| 42 to 43 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 65 |
| Thermal Shock Resistance, points | 16 to 23 | |
| 16 to 17 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 94.6 to 98 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 16 to 18 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 | |
| 0.15 to 0.4 |
| Iron (Fe), % | 67.9 to 75 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 0.5 to 1.2 |
| Manganese (Mn), % | 5.5 to 7.5 | |
| 0.4 to 1.0 |
| Nickel (Ni), % | 3.5 to 5.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 1.0 to 1.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |