AISI 201L Stainless Steel vs. 88-silver 12-tin-oxide
AISI 201L stainless steel belongs to the iron alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is AISI 201L stainless steel and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 84 to 86 |
| Elongation at Break, % | 22 to 46 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 24 to 70 |
| Shear Strength, MPa | 520 to 660 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 1040 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 290 to 790 | |
| 110 to 260 |