AISI 201LN Stainless Steel vs. 6005 Aluminum
AISI 201LN stainless steel belongs to the iron alloys classification, while 6005 aluminum belongs to the aluminum alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AISI 201LN stainless steel and the bottom bar is 6005 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 210 to 320 | |
90 to 95 |
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
68 |
Elongation at Break, % | 25 to 51 | |
9.5 to 17 |
Fatigue Strength, MPa | 340 to 540 | |
55 to 95 |
Poisson's Ratio | 0.28 | |
0.33 |
Shear Modulus, GPa | 77 | |
26 |
Shear Strength, MPa | 530 to 680 | |
120 to 210 |
Tensile Strength: Ultimate (UTS), MPa | 740 to 1060 | |
190 to 310 |
Tensile Strength: Yield (Proof), MPa | 350 to 770 | |
100 to 280 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
410 |
Maximum Temperature: Mechanical, °C | 880 | |
160 |
Melting Completion (Liquidus), °C | 1410 | |
650 |
Melting Onset (Solidus), °C | 1370 | |
610 |
Specific Heat Capacity, J/kg-K | 480 | |
900 |
Thermal Conductivity, W/m-K | 15 | |
180 to 200 |
Thermal Expansion, µm/m-K | 17 | |
23 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
54 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
180 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 12 | |
9.5 |
Density, g/cm3 | 7.7 | |
2.7 |
Embodied Carbon, kg CO2/kg material | 2.6 | |
8.3 |
Embodied Energy, MJ/kg | 38 | |
150 |
Embodied Water, L/kg | 140 | |
1180 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 230 to 310 | |
27 to 36 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 1520 | |
77 to 550 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
51 |
Strength to Weight: Axial, points | 27 to 38 | |
20 to 32 |
Strength to Weight: Bending, points | 24 to 30 | |
28 to 38 |
Thermal Diffusivity, mm2/s | 4.0 | |
74 to 83 |
Thermal Shock Resistance, points | 16 to 23 | |
8.6 to 14 |
Alloy Composition
Aluminum (Al), % | 0 | |
97.5 to 99 |
Carbon (C), % | 0 to 0.030 | |
0 |
Chromium (Cr), % | 16 to 17.5 | |
0 to 0.1 |
Copper (Cu), % | 0 to 1.0 | |
0 to 0.1 |
Iron (Fe), % | 67.9 to 73.5 | |
0 to 0.35 |
Magnesium (Mg), % | 0 | |
0.4 to 0.6 |
Manganese (Mn), % | 6.4 to 7.5 | |
0 to 0.1 |
Nickel (Ni), % | 4.0 to 5.0 | |
0 |
Nitrogen (N), % | 0.1 to 0.25 | |
0 |
Phosphorus (P), % | 0 to 0.045 | |
0 |
Silicon (Si), % | 0 to 0.75 | |
0.6 to 0.9 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Titanium (Ti), % | 0 | |
0 to 0.1 |
Zinc (Zn), % | 0 | |
0 to 0.1 |
Residuals, % | 0 | |
0 to 0.15 |