AISI 204 Stainless Steel vs. AWS E90C-B9
Both AISI 204 stainless steel and AWS E90C-B9 are iron alloys. They have 84% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AISI 204 stainless steel and the bottom bar is AWS E90C-B9.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 23 to 39 | |
| 18 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1100 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1080 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 15 | |
| 25 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 7.0 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 35 | |
| 37 |
| Embodied Water, L/kg | 130 | |
| 91 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 to 250 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 2940 | |
| 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 27 to 40 | |
| 25 |
| Strength to Weight: Bending, points | 24 to 31 | |
| 23 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 6.9 |
| Thermal Shock Resistance, points | 16 to 24 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.040 |
| Carbon (C), % | 0 to 0.030 | |
| 0.080 to 0.13 |
| Chromium (Cr), % | 15 to 17 | |
| 8.0 to 10.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.2 |
| Iron (Fe), % | 69.6 to 76.4 | |
| 84.4 to 90.9 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 0 to 1.2 |
| Molybdenum (Mo), % | 0 | |
| 0.85 to 1.2 |
| Nickel (Ni), % | 1.5 to 3.0 | |
| 0 to 0.8 |
| Niobium (Nb), % | 0 | |
| 0.020 to 0.1 |
| Nitrogen (N), % | 0.15 to 0.3 | |
| 0.030 to 0.070 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0.15 to 0.3 |
| Residuals, % | 0 | |
| 0 to 0.5 |