AISI 204 Stainless Steel vs. EN 1.4107 Stainless Steel
Both AISI 204 stainless steel and EN 1.4107 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AISI 204 stainless steel and the bottom bar is EN 1.4107 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 23 to 39 | |
| 18 to 21 |
| Fatigue Strength, MPa | 320 to 720 | |
| 260 to 350 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1100 | |
| 620 to 700 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1080 | |
| 400 to 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 850 | |
| 740 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1450 |
| Melting Onset (Solidus), °C | 1370 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 27 |
| Thermal Expansion, µm/m-K | 17 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 7.5 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 2.1 |
| Embodied Energy, MJ/kg | 35 | |
| 30 |
| Embodied Water, L/kg | 130 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 to 250 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 2940 | |
| 420 to 840 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 27 to 40 | |
| 22 to 25 |
| Strength to Weight: Bending, points | 24 to 31 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 7.2 |
| Thermal Shock Resistance, points | 16 to 24 | |
| 22 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.1 |
| Chromium (Cr), % | 15 to 17 | |
| 11.5 to 12.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 69.6 to 76.4 | |
| 83.8 to 87.2 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 1.5 to 3.0 | |
| 0.8 to 1.5 |
| Nitrogen (N), % | 0.15 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0 to 0.080 |