AISI 204 Stainless Steel vs. EN 1.4640 Stainless Steel
Both AISI 204 stainless steel and EN 1.4640 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is AISI 204 stainless steel and the bottom bar is EN 1.4640 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 330 | |
| 190 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 23 to 39 | |
| 51 |
| Fatigue Strength, MPa | 320 to 720 | |
| 230 to 250 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Shear Strength, MPa | 500 to 700 | |
| 440 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1100 | |
| 620 to 650 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1080 | |
| 240 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 280 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 850 | |
| 930 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1420 |
| Melting Onset (Solidus), °C | 1370 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 15 |
| Thermal Expansion, µm/m-K | 17 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.9 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 14 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 35 | |
| 40 |
| Embodied Water, L/kg | 130 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 20 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 240 to 250 | |
| 250 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 to 2940 | |
| 150 to 170 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 27 to 40 | |
| 22 to 23 |
| Strength to Weight: Bending, points | 24 to 31 | |
| 21 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 4.0 |
| Thermal Shock Resistance, points | 16 to 24 | |
| 14 to 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.030 to 0.080 |
| Chromium (Cr), % | 15 to 17 | |
| 18 to 19 |
| Copper (Cu), % | 0 | |
| 1.3 to 2.0 |
| Iron (Fe), % | 69.6 to 76.4 | |
| 67.4 to 73.6 |
| Manganese (Mn), % | 7.0 to 9.0 | |
| 1.5 to 4.0 |
| Nickel (Ni), % | 1.5 to 3.0 | |
| 5.5 to 6.9 |
| Nitrogen (N), % | 0.15 to 0.3 | |
| 0.030 to 0.11 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |