AISI 205 Stainless Steel vs. EN 1.1133 Steel
Both AISI 205 stainless steel and EN 1.1133 steel are iron alloys. They have 67% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AISI 205 stainless steel and the bottom bar is EN 1.1133 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 440 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 51 | |
| 19 to 24 |
| Fatigue Strength, MPa | 410 to 640 | |
| 230 to 310 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 560 to 850 | |
| 370 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 1430 | |
| 580 to 620 |
| Tensile Strength: Yield (Proof), MPa | 450 to 1100 | |
| 320 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 400 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1460 |
| Melting Onset (Solidus), °C | 1340 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 2.1 |
| Density, g/cm3 | 7.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.5 |
| Embodied Energy, MJ/kg | 37 | |
| 19 |
| Embodied Water, L/kg | 150 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 430 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 3060 | |
| 270 to 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 26 | |
| 24 |
| Strength to Weight: Axial, points | 29 to 52 | |
| 21 to 22 |
| Strength to Weight: Bending, points | 25 to 37 | |
| 20 to 21 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 18 to 19 |
Alloy Composition
| Carbon (C), % | 0.12 to 0.25 | |
| 0.17 to 0.23 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 0 to 0.4 |
| Iron (Fe), % | 62.6 to 68.1 | |
| 96.9 to 98.8 |
| Manganese (Mn), % | 14 to 15.5 | |
| 1.0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 1.0 to 1.7 | |
| 0 to 0.4 |
| Nitrogen (N), % | 0.32 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.035 |