AISI 205 Stainless Steel vs. EN 1.4662 Stainless Steel
Both AISI 205 stainless steel and EN 1.4662 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AISI 205 stainless steel and the bottom bar is EN 1.4662 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 11 to 51 | |
| 28 |
| Fatigue Strength, MPa | 410 to 640 | |
| 430 to 450 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 77 | |
| 79 |
| Shear Strength, MPa | 560 to 850 | |
| 520 to 540 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 1430 | |
| 810 to 830 |
| Tensile Strength: Yield (Proof), MPa | 450 to 1100 | |
| 580 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 410 | |
| 440 |
| Maximum Temperature: Mechanical, °C | 880 | |
| 1090 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1430 |
| Melting Onset (Solidus), °C | 1340 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 16 |
| Density, g/cm3 | 7.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 3.2 |
| Embodied Energy, MJ/kg | 37 | |
| 45 |
| Embodied Water, L/kg | 150 | |
| 170 |
Common Calculations
| PREN (Pitting Resistance) | 23 | |
| 33 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 430 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 3060 | |
| 840 to 940 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 26 | |
| 25 |
| Strength to Weight: Axial, points | 29 to 52 | |
| 29 to 30 |
| Strength to Weight: Bending, points | 25 to 37 | |
| 25 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 22 |
Alloy Composition
| Carbon (C), % | 0.12 to 0.25 | |
| 0 to 0.030 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 23 to 25 |
| Copper (Cu), % | 0 | |
| 0.1 to 0.8 |
| Iron (Fe), % | 62.6 to 68.1 | |
| 62.6 to 70.2 |
| Manganese (Mn), % | 14 to 15.5 | |
| 2.5 to 4.0 |
| Molybdenum (Mo), % | 0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 1.0 to 1.7 | |
| 3.0 to 4.5 |
| Nitrogen (N), % | 0.32 to 0.4 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0050 |