AISI 205 Stainless Steel vs. EN 1.4742 Stainless Steel

Both AISI 205 stainless steel and EN 1.4742 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AISI 205 stainless steel and the bottom bar is EN 1.4742 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 440
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11 to 51
17
Fatigue Strength, MPa 410 to 640
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 560 to 850
370
Tensile Strength: Ultimate (UTS), MPa 800 to 1430
600
Tensile Strength: Yield (Proof), MPa 450 to 1100
300

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 880
1000
Melting Completion (Liquidus), °C 1380
1420
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 480
490
Thermal Expansion, µm/m-K 18
11

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.0
Density, g/cm3 7.6
7.6
Embodied Carbon, kg CO2/kg material 2.6
2.2
Embodied Energy, MJ/kg 37
32
Embodied Water, L/kg 150
130

Common Calculations

PREN (Pitting Resistance) 23
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150 to 430
84
Resilience: Unit (Modulus of Resilience), kJ/m3 510 to 3060
230
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 26
25
Strength to Weight: Axial, points 29 to 52
22
Strength to Weight: Bending, points 25 to 37
21
Thermal Shock Resistance, points 16 to 29
21

Alloy Composition

Aluminum (Al), % 0
0.7 to 1.2
Carbon (C), % 0.12 to 0.25
0 to 0.12
Chromium (Cr), % 16.5 to 18.5
17 to 19
Iron (Fe), % 62.6 to 68.1
77.2 to 81.6
Manganese (Mn), % 14 to 15.5
0 to 1.0
Nickel (Ni), % 1.0 to 1.7
0
Nitrogen (N), % 0.32 to 0.4
0
Phosphorus (P), % 0 to 0.060
0 to 0.040
Silicon (Si), % 0 to 1.0
0.7 to 1.4
Sulfur (S), % 0 to 0.030
0 to 0.015