AISI 205 Stainless Steel vs. Type 2 Magnetic Alloy
Both AISI 205 stainless steel and Type 2 magnetic alloy are iron alloys. They have 53% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AISI 205 stainless steel and the bottom bar is Type 2 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 51 | |
| 2.0 to 38 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 77 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 800 to 1430 | |
| 510 to 910 |
| Tensile Strength: Yield (Proof), MPa | 450 to 1100 | |
| 260 to 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 270 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1420 |
| Melting Onset (Solidus), °C | 1340 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 33 |
| Density, g/cm3 | 7.6 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 5.9 |
| Embodied Energy, MJ/kg | 37 | |
| 81 |
| Embodied Water, L/kg | 150 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 430 | |
| 18 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 3060 | |
| 170 to 2010 |
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 26 | |
| 23 |
| Strength to Weight: Axial, points | 29 to 52 | |
| 17 to 30 |
| Strength to Weight: Bending, points | 25 to 37 | |
| 17 to 25 |
| Thermal Shock Resistance, points | 16 to 29 | |
| 16 to 29 |
Alloy Composition
| Carbon (C), % | 0.12 to 0.25 | |
| 0 to 0.050 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 0 to 0.3 |
| Cobalt (Co), % | 0 | |
| 0 to 0.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 62.6 to 68.1 | |
| 48.2 to 53 |
| Manganese (Mn), % | 14 to 15.5 | |
| 0 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 1.0 to 1.7 | |
| 47 to 49 |
| Nitrogen (N), % | 0.32 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.060 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |