AISI 301L Stainless Steel vs. 92-silver 8-tin-oxide
AISI 301L stainless steel belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (27, in this case) are not shown.
For each property being compared, the top bar is AISI 301L stainless steel and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 76 to 80 |
| Elongation at Break, % | 22 to 50 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 210 to 300 | |
| 62 to 110 |
| Shear Strength, MPa | 440 to 660 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 1040 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 250 to 790 | |
| 120 to 300 |